Covestro Bayblend FR 3310 TV
An easy-flowing, flame-retardant 15% glass fiber PC+ABS blend engineered for safety, performance, and superior processability in modern electronics and appliance manufacturing.
This grade offers increased heat resistance and is specifically designed to meet the stringent safety standards of the industry, making it the ideal choice for television housings, IT equipment, and more.
Key Features & Benefits
Excellent Flame Retardancy
Achieves UL 94 V-0 classification at 1.5 mm, providing critical safety for electronic enclosures and consumer peace of mind.
High Heat Resistance
Maintains structural integrity at elevated temperatures with a Vicat softening point of 110 °C, ensuring durability and long service life.
Easy Flowability
Excellent melt flow characteristics allow for complex part design and thin-wall applications, boosting manufacturing efficiency.
Ideal for Demanding Applications
With its balanced profile of safety, durability, and design freedom, Bayblend® FR3110 TV is the premier choice for a wide range of electronic and electrical products.
-
Television & Monitor Housings
Perfect for bezels, back covers, and stands where aesthetics and safety are paramount.
-
IT & Consumer Electronics
Reliable enclosures for printers, routers, game consoles, and other connected devices.
-
Electrical Appliance Components
Used in components where high heat resistance and electrical insulation properties are required.
Ready to Elevate Your Product?
Discover how Bayblend® FR3110 TV can bring superior safety, performance, and manufacturing efficiency to your next project. Contact our specialists today.
Technical Specifications
Rheological Properties
| Property | Test Condition | Value | Unit | Standard |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 240 °C; 5 kg | 29 | cm³/10 min | ISO 1133-1 |
| Molding Shrinkage, Parallel | 150x105x3 mm; 240°C/80°C | 0.50 - 0.70 | % | ISO 2577 |
| Molding Shrinkage, Normal | 150x105x3 mm; 240°C/80°C | 0.50 - 0.70 | % | ISO 2577 |
Mechanical Properties (at 23 °C / 50% r.h.)
| Property | Test Condition | Value | Unit | Standard |
|---|---|---|---|---|
| Tensile Modulus | 1 mm/min | 2,600 | MPa | ISO 527-1,-2 |
| Yield Stress | 50 mm/min | 60 | MPa | ISO 527-1,-2 |
| Yield Strain | 50 mm/min | 4 | % | ISO 527-1,-2 |
| Nominal Strain at Break | 50 mm/min | > 50 | % | ISO 527-1,-2 |
| Stress at Break | 50 mm/min | 50 | MPa | ISO 527-1,-2 |
| Izod Notched Impact Strength | 23 °C | 12 | kJ/m² | ISO 180/A |
Thermal Properties
| Property | Test Condition | Value | Unit | Standard |
|---|---|---|---|---|
| Temp. of Deflection under Load (HDT/B) | 0.45 MPa | 101 | °C | ISO 75-1,-2 |
| Temp. of Deflection under Load (HDT/A) | 1.80 MPa | 84 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (VST/B120) | 50 N; 120 °C/h | 110 | °C | ISO 306 |
| Vicat Softening Temperature (VST/B50) | 50 N; 50 °C/h | 108 | °C | ISO 306 |
| Coeff. of Linear Thermal Expansion, Parallel | 23 to 55 °C | 0.68 | 10⁻⁴/K | ISO 11359-1,-2 |
| Coeff. of Linear Thermal Expansion, Normal | 23 to 55 °C | 0.68 | 10⁻⁴/K | ISO 11359-1,-2 |
Flammability & Other Properties
| Property | Test Condition | Value | Unit | Standard |
|---|---|---|---|---|
| UL 94 Flame Classification | 1.5 mm | V-0 | Class | UL 94 |
| Density | - | 1280 | kg/m³ | ISO 1183-1 |
Recommended Processing Conditions
Drying
| Drying Method | Dry Air or Dehumidifying Dryer |
| Drying Temperature | 80 °C |
| Drying Time | 4 h |
| Max. Moisture Content | ≤ 0.02 % |
Note: Pellets must be dried prior to processing to prevent hydrolytic degradation.
Injection Molding
| Melt Temperature | 240 - 280 °C (Standard: 260 °C) |
| Mold Temperature | 60 - 90 °C |
| Back Pressure | 50 - 150 bar |
| Screw Speed | 0.05 - 0.2 m/s |